Micro-hardness and mineral loss of enamel lesions after infiltration with various resins: Influence of infiltrant composition and application frequency in vitro
چکیده:   (1789 مشاهده)

 Objectives

  The aim of this in vitro study was to evaluate the influence of infiltrant composition and application frequency on micro-hardness and lesion progression after resin infiltration of artificial enamel lesions.

 Methods

 In each of 100 bovine enamel samples, three artificial caries lesions were created (pH=4.95, 50 days). After etching two of the lesions (37% phosphoric acid) specimens were randomly allocated to five infiltrants (four experimental infiltrants with different monomer and solvent compositions and penetration coefficients, and one commercial infiltrant [Icon, DMG]). Lesions were then infiltrated and light-cured, and infiltration repeated afterwards for one of the lesions. Infiltrated samples were cut into halves, with one half being demineralised for further 50 days. Micro-hardness (VHN) and integrated mineral loss (ΔZ) were evaluated at baseline and after second demineralisation. Repeated measures ANOVA and paired t-tests were used to analyse influence of material composition and application frequency on micro-hardness and lesion progression (integrated mineral loss difference ΔΔZ).

 Results

 Resin infiltration significantly increased micro-hardness and reduced lesion progression compared to untreated artificial lesions (p<0.05, t-test). Neither micro-hardness nor lesion progression were significantly influenced by material composition (p>0.05, ANOVA). In contrast, twice application resulted in significantly increased micro-hardness and demineralisation resistance of infiltrated lesions (p<0.05, ANOVA).

 Conclusion

  Resin infiltration significantly improves micro-hardness and demineralisation resistance of enamel lesions these effects are significantly enhanced if resins are applied twice. Experimental resins did not outperform the commercial infiltrant.

  Clinical significance

  This in vitro study demonstrated that resin infiltration significantly increases both micro-hardness and demineralisation resistance of enamel caries lesions. Twice application of the infiltrant seems to increase these effects. In contrast, the composition of the infiltrant had no significant influence on investigated parameters.


 Source: Journal of Dentistry

 Full Text

واژه‌های کلیدی: Caries infiltration، Infiltrant، Resin، Solvent، Micro-hardness، Application
     
نوع مطالعه: پژوهشي | موضوع مقاله: پریودنتولوژی
دریافت: 1392/7/16 | انتشار: 1390/10/25
ارسال نظر درباره این مقاله
نام کاربری یا پست الکترونیک شما:

CAPTCHA


XML     Print


Download citation:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:


Micro-hardness and mineral loss of enamel lesions after infiltration with various resins: Influence of infiltrant composition and application frequency in vitro. 1. 1390; 6 (6)

URL: http://idai.ir/article-1-2187-fa.html



بازنشر اطلاعات
Creative Commons License این مقاله تحت شرایط Creative Commons Attribution-NonCommercial 4.0 International License قابل بازنشر است.
دوره 6، شماره 6 - ( پریودنتولوژی 1390 ) برگشت به فهرست نسخه ها
جامعه اسلامی دندانپزشکان Islamic Dental Association of IRAN

کلیه حقوق سایت متعلق به جامعه اسلامی دندانپزشکان ایران است. تماس با ما

Persian site map - English site map - Created in 0.06 seconds with 37 queries by YEKTAWEB 4710