The effect of mechanical load cycling and polishing time on microleakage of class V glass-ionomer and composite restorations:A scanning electron microscopy evaluation
چکیده:   (1650 مشاهده)
Background: Microleakage is one of the challenging concerns in direct fi lling restorations. Understanding of its related factors is important in clinical practice. The aim of this study was scanning electron microscopy (SEM) evaluation of marginal integrity in three types of tooth-colored restorative materials in class V cavity preparations and the effect of load cycling and polishing time on the microleakage. 
  Materials and Methods: In this in vitro experimental study, class V cavity preparations were prepared on the buccal and lingual surfaces of 60 bovine incisors. The specimens were divided into three groups each containing 20 teeth: group 1: Filtek Z350, Group 2: Fuji IX/G Coat Plus, Group 3: Fuji II LC/GC varnish. In each group, 2 subgroups (n = 20) were established based on fi nishing time (immediate or delayed by 24 h). All specimens were thermocycled (×2,000, 5-50°C). In each sub groups, half of the teeth were load cycled. Epoxy resin replicas of 24 specimens were evaluated under fi eld emission-SEM and interfacial gaps were measured. All teeth were then immersed in 0.5% basic fuchsin dye for 24 h, sectioned and observed under stereomicroscope. Data were analyzed with Kruskal-Wallis’ test and Mann-Whitney U test and a comparison between incisal and cervical microleakage was made with Wilcoxon test. P < 0.05 was considered as signifi cant.
Results: Load cycling and fi lling material had a signifi cant effect on microleakage, but polishing time did not. Cervical microleakage in Z350/load cycle/immediate polish and Fuji IX/load cycle/immediate or delayed polish and Fuji IX/no load cycle/immediate polish were signifi cantly higher than incisal microleakage. 
  Conclusion: It was concluded that the cervical sealing ability of Fuji IX under load cycling was better than Fuji II LC. Under load cycling and immediate polishing Z350 showed better marginal integrity than both Fuji II LC and Fuji IX. The immediate polishing didn’t cause a statistically signifi cant increase in microleakage of evaluated tooth-colored class V restorations.

Source: Dental Research Journal

Full Text

واژه‌های کلیدی: Composite resins، dental leakage، dental polishing، glass ionomer cements
     
نوع مطالعه: پژوهشي | موضوع مقاله: ترمیمی
دریافت: 1394/6/24 | پذیرش: 1394/6/24 | انتشار: 1394/6/24
ارسال نظر درباره این مقاله
نام کاربری یا پست الکترونیک شما:

CAPTCHA


XML     Print


Download citation:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:


The effect of mechanical load cycling and polishing time on microleakage of class V glass-ionomer and composite restorations:A scanning electron microscopy evaluation. 1. 1390;

URL: http://idai.ir/article-1-3459-fa.html



بازنشر اطلاعات
Creative Commons License این مقاله تحت شرایط Creative Commons Attribution-NonCommercial 4.0 International License قابل بازنشر است.
جلد 0 - ترمیمی برگشت به فهرست نسخه ها
جامعه اسلامی دندانپزشکان Islamic Dental Association of IRAN

کلیه حقوق سایت متعلق به جامعه اسلامی دندانپزشکان ایران است. تماس با ما

Persian site map - English site map - Created in 0.06 seconds with 37 queries by YEKTAWEB 4710