.Influence of veneer thickness on residual stress profile in veneering ceramic: Measurement by hole-drilling
چکیده:   (2825 مشاهده)
Objectives

 The veneering process of frameworks induces residual stresses and can initiate cracks when combined with functional stresses. The stress distribution within the veneering ceramic as a function of depth is a key factor influencing failure by chipping. This is a well-known problem with Yttria-tetragonal-zirconia-polycrystal based fixed partial dentures. The objective of this study is to investigate the influence of veneer thickness on the stress profile in zirconia- and metal-based structures.

Methods

 The hole-drilling method, often used for engineering measurements, was adapted for use with veneering ceramic. The stress profile was measured in bilayered disc samples of 20AWT IMAGEmm diameter, with a 1AWT IMAGEmm thick zirconia or metal framework. Different veneering ceramic thicknesses were performed: 1AWT IMAGEmm, 1.5AWT IMAGEmm, 2AWT IMAGEmm, 2.5AWT IMAGEmm and 3AWT IMAGEmm.

Results

 All samples exhibited the same type of stress vs. depth profile, starting with compressive at the ceramic surface, decreasing with depth up to 0.5–1.0AWT IMAGEmm from the surface, and then becoming compressive again near the framework, except for the 1.5AWT IMAGEmm-veneered zirconia samples which exhibited interior tensile stresses. Stresses in the surface of metal samples were not influenced by veneer thickness. Variation of interior stresses at 1.2AWT IMAGEmm from the surface in function of veneer thickness was inverted for metal and zirconia samples.

Significance

 Veneer thickness influences in an opposite way the residual stress profile in metal- and in zirconia-based structures. A three-step approach and the hypothesis of the crystalline transformation are discussed to explain the less favorable residual stress development in zirconia samples.


  Source: Dental Materials

  Full text

     
نوع مطالعه: پژوهشي | موضوع مقاله: ترمیمی
دریافت: 1390/11/20 | پذیرش: 1394/9/25 | انتشار: 1394/9/25
ارسال نظر درباره این مقاله
نام کاربری یا پست الکترونیک شما:

CAPTCHA


XML   English Abstract   Print


Download citation:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:

K. Mainjot A, S. Schajer G, J. Vanheusden A, J. Sadoun M. .Influence of veneer thickness on residual stress profile in veneering ceramic: Measurement by hole-drilling. 3 2012;
URL: http://idai.ir/article-1-272-fa.html

.Influence of veneer thickness on residual stress profile in veneering ceramic: Measurement by hole-drilling. 1. 1390;

URL: http://idai.ir/article-1-272-fa.html



بازنشر اطلاعات
Creative Commons License این مقاله تحت شرایط Creative Commons Attribution-NonCommercial 4.0 International License قابل بازنشر است.
جلد 0 - ترمیمی برگشت به فهرست نسخه ها
جامعه اسلامی دندانپزشکان Islamic Dental Association of IRAN

کلیه حقوق سایت متعلق به جامعه اسلامی دندانپزشکان ایران است. تماس با ما

Persian site map - English site map - Created in 0.03 seconds with 37 queries by YEKTAWEB 4712