Objectives

  To determine the resin-strengthening dependence of a soda-lime-glass analogue for dental porcelain as a function of biaxial flexure strength (BFS), test crosshead rate and cementation seating load.

 Methods

 Disc-shaped soda-lime glass specimens were divided into twelve groups (n=24), alumina particle air abraded and hydrofluoric acid-etched. Specimens (Groups A–D) were stored in a desiccator prior to testing at crosshead rates of 0.01, 0.1, 1 and 10mm/min, respectively. The remaining specimens were silane treated, Rely-X Veneer resin-coated with a seating load of 5N (Groups E–H) and 30N (Groups I–L) prior to light irradiation at 480±20mW/cm2, 24h dry storage and BFS testing at 0.01, 0.1, 1 and 10mm/min, respectively. A linear logarithmic regression curve was fit to the raw data to elucidate static fatigue effects of the soda-lime-glass. Analysis of group means was performed utilising a general linear model univariate analysis and post hoc all paired Tukey tests (P<0.05).

 Results

  The linear logarithmic regression curve demonstrated the static fatigue effects of the soda-lime-glass analogue. Rely-X Veneer resin-coating (Groups E–L) resulted in significant increases in the mean BFS data for all crosshead rates examined (all P<0.001). However, the pattern of rate dependence effects on resin-cementation deviated from the log relationship observed with the uncoated controls.

 Conclusion

  This study further highlights that when slow crack growth is simulated during testing, valuable insights into the significant modification of a hereto well described phenomenon such as resin-strengthening mediated by the resin–ceramic hybrid layer is provided.

 Source: Journal of Dentistry

 Full Text