Temperature-dependence of creep behaviour of dental resin-composites
چکیده:   (1483 مشاهده)

 Objectives

 To determine the effect of temperature, over a clinically relevant range, on the creep behaviour of a set of conventional and flowable resin-composites including two subgroups having the same resin matrix and varied filler loading.

 Methods

  Eight dental resin-composites: four flowable and four conventional were investigated. Stainless steel split moulds (4mm×6mm) were used to prepare cylindrical specimens for creep examination. Specimens were irradiated in the moulds in layers of 2mm thickness (40s each), as well as from the radial direction after removal from the moulds, using a light-curing unit with irradiance of 650mW/cm2. A total of 15 specimens from each material were prepared and divided into three groups (n=5) according to the temperature Group I: (23°C), Group II: (37°C) and Group III: (45°C). Each specimen was loaded (20MPa) for 2h and unloaded for 2h. Creep was measured continuously over the loading and unloading periods.

 Results

  At higher temperatures greater creep and permanent set were recorded. The lowest mean creep occurred with GS and GH resin-composites. Percentage of creep recovery decreased at higher temperatures. At 23°C, the materials exhibited comparable creep. At 37°C and 45°C, however, there was a greater variation between materials. For all resin-composites, there was a strong linear correlation with temperature for both creep and permanent set.

  Conclusions

  Creep parameters of resin-composites are sensitive to temperature increase from 23 to 45°C, as can occur intra-orally. For a given resin matrix, creep decreased with higher filler loading.


 Source: Journal of Dentistry

 Full Text

واژه‌های کلیدی: Creep and recovery، Resin-composites، Temperature، Filler loading، Resin matrix
     
نوع مطالعه: پژوهشي | موضوع مقاله: ترمیمی
دریافت: 1392/7/13 | پذیرش: 1394/9/25 | انتشار: 1394/9/25
ارسال نظر درباره این مقاله
نام کاربری یا پست الکترونیک شما:

CAPTCHA


XML     Print


Download citation:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:


Temperature-dependence of creep behaviour of dental resin-composites. 1. 1390;

URL: http://idai.ir/article-1-2155-fa.html



بازنشر اطلاعات
Creative Commons License این مقاله تحت شرایط Creative Commons Attribution-NonCommercial 4.0 International License قابل بازنشر است.
جلد 0 - ترمیمی برگشت به فهرست نسخه ها
جامعه اسلامی دندانپزشکان Islamic Dental Association of IRAN

کلیه حقوق سایت متعلق به جامعه اسلامی دندانپزشکان ایران است. تماس با ما

Persian site map - English site map - Created in 0.06 seconds with 37 queries by YEKTAWEB 4710