fa In Vitro Effects of Different Surface Preparation Techniques on Shear Bond Strength of Direct to Indirect Composite Resin ترمیمی Cosmetic and Restorative Dentistry پژوهشي Research <b> Objective: </b><div>Repair of an indirect restoration is usually preferred over its replacement. This study aimed to evaluate the effect of silane in different surface preparation techniques on the bond strength of direct to indirect composite resin.</div><div><b> Methods:</b></div><div> For this in-vitro experimental study, 48 indirect composite cubes were fabricated, divided into 4 groups of 12 and subjected to the following preparation techniques: Group 1. Sandblasting with 50μaluminum oxide particles (SB), Group 2. Sandblasting + silanization (SB+Sil), Group 3. Etching with 9.5% hydrofluoric (HF) acid, Group 4. Etching with 9.5% HF acid +silanization (HF+Sil). Before the restoration process, specimens were subjected to 500 thermal cycles and received surface preparations. Single Bond adhesive was applied to the surface in all groups. Specimens were restored with direct composite resin and stored in an incubator at 37°C for 24h. Fracture was induced in the specimens by an Instron machine and the shear bond strength was measured. Data were converted to mega Pascal and analyzed using two-way ANOVA. </div><div>  <b>Results:</b></div><div> The highest shear bond strength was 13.85±2.75 MPa and belonged to group 1 while the lowest bond strength was 8.43±1.35MPa and observed in group 2. </div><div>  <b>Conclusion:</b></div><div> Based on the obtained results, composite surface preparation by sandblasting yields more favorable results than HF acid etching and application of silane can also increase the bond strength.</div><hr><p class="MsoNormal" dir="rtl"><b><span lang="FA" style="font-family: Tahoma, sans-serif">منبع:</span></b><span lang="FA" style="font-family: Tahoma, sans-serif"> مجله دانشکده دندانپزشکی دانشگاه علوم پزشکی شهید بهشتی<o:p /></span></p> <p class="MsoNormal" dir="rtl"><span lang="FA" style="font-family: Tahoma, sans-serif"><a href="http://jds.sbmu.ac.ir/browse.php?a_id=1242&sid=1&slc_lang=en" target="_blank"><font color="#0000ff">متن کامل</font></a></span><span lang="FA" style="font-size: 12pt line-height: 115% font-family: Tahoma, sans-serif"><o:p /></span></p> Shear bond strength, Silane, Surface preparation, Dentin bonding agents, Stress, 0 0 http://idai.ir/browse.php?a_code=A-10-32-2915&slc_lang=fa&sid=1 Azita Kaviani 100319475328460013565 100319475328460013565 No Dept. of Operative Dentistry, Dental School, Jondi Shapour University of Medical Sciences, Ahvaz, Iran Naghmeh Gharizadeh 100319475328460013566 100319475328460013566 No Dept. of Operative Dentistry, Dental School, Jondi Shapour University of Medical Sciences, Ahvaz, Iran Hengameh Alinejad hengamehalinejad@yahoo.com 100319475328460013567 100319475328460013567 Yes Dept. of Operative Dentistry, Dental School, Jondi Shapour University of Medical Sciences, Ahvaz, Iran Reyhaneh Moosavi 100319475328460013568 100319475328460013568 No