fa Shear bond strength of porcelain laminate veneers to enamel, dentine and enamel–dentine complex bonded with different adhesive luting systems ترمیمی Cosmetic and Restorative Dentistry پژوهشي Research <p> <strong>Objectives</strong></p><p>  The aim of this study was to evaluate the shear bond strength of porcelain laminate veneers to 3 different surfaces by means of enamel, dentine, and enamel–dentine complex. </p><p> <strong>Methods</strong> </p><p> One hundred thirty-five extracted human maxillary central teeth were used, and the teeth were randomly divided into 9 groups (n=15). The teeth were prepared with 3 different levels for bonding surfaces of enamel (E), dentine (D), and enamel–dentine complex (E–D). Porcelain discs (IPS e.max Press, Ivoclar Vivadent) of 2mm in thickness and 4mm in diameter were luted to the tooth surfaces by using 2 light-curing (RelyX Veneer [RV], 3M ESPE Variolink Veneer [VV], Ivoclar Vivadent) and a dual-curing (Variolink II [V2], Ivoclar Vivadent) adhesive systems according to the manufacturers’ instructions. Shear bond strength test was performed in a universal testing machine at 0.5mm/min until bonding failure. Failure modes were determined under a stereomicroscope, and fracture surfaces were evaluated with a scanning electron microscope. The data were statistically analysed (SPSS 17.0) (p=0.05). </p><p> <strong>Results</strong></p><p>  Group RV-D exhibited the lowest bond strength value (5.42±6.6MPa). There was statistically no difference among RV-D, V2-D (13.78±8.8MPa) and VV-D (13.84±6.2MPa) groups (p>0.05). Group VV-E exhibited the highest bond strength value (24.76±8.8MPa). <strong></strong></p><p> <strong>Conclusions</strong></p><p>  The type of tooth structure affected the shear bond strength of the porcelain laminate veneers to the 3 different types of tooth structures (enamel, dentine, and enamel–dentine complex). Clinical significance When dentine exposure is necessary during preparation, enough sound enamel must be protected as much as possible to maintain a good bonding to obtain maximum bond strength, preparation margins should be on sound enamel. </p><hr><p></p><p> <strong>Source: </strong>Journal of Dentistry</p><p> <a href="http://www.jodjournal.com/article/S0300-5712(12)00088-7/abstract" target="_blank"><font color="#0000ff">Full Text</font></a></p> Porcelain laminate veneers, Dentine exposure, Adhesives 0 0 http://idai.ir/browse.php?a_code=A-10-32-2101&slc_lang=fa&sid=1 Elif Öztürk 10031947532846009844 10031947532846009844 Yes University of Kocaeli, Faculty of Dentistry, Department of Restorative Dentistry, Yuvacik/Basiskele, Kocaeli, Turkey Şükran Bolay 10031947532846009845 10031947532846009845 No Hacettepe University, Faculty of Dentistry, Department of Restorative Dentistry, Sihhiye-06100, Ankara, Turkey Reinhard Hickel 10031947532846009846 10031947532846009846 No Ludwig-Maximilians-University, School of Dentistry, Department of Restorative Dentistry, Goethestrasse 70, 80336 Munich, Germany Nicoleta Ilie 10031947532846009847 10031947532846009847 No Ludwig-Maximilians-University, School of Dentistry, Department of Restorative Dentistry, Goethestrasse 70, 80336 Munich, Germany