Cyanoacrylate-POSS nanocomposites: Novel adhesives with improved properties for dental applications


Parastoo Fadaie,Mohammad Atai,*Mohammad Imani,AkbarKarkhaneh,Samaneh Ghasaban

*Iran Polymer and Petrochemical Institute,Tehran,Iran


Abstract

Objectives: This study evaluates the effect of incorporation of an acrylate polyhedral oligomeric silsesquioxane nanostructure (APOSS) on the physical and mechanical properties and hydrolytic stability of octyl cyanoacrylate (CA) adhesives.

Materials and methods: CA was photopolymerized under irradiation of visible light using 1- phenyle-1,2-propandione (PPD), and 2,3-botanedione (BD) as photoinitiators. Following the polymerization shrinkage kinetics of the adhesives, the initiator concentration was optimized. Mechanical properties of the bulk CA–APOSS nanocomposites, including flexural strength and modulus, were investigated. Miroshear bond strength of dental composite bonded to human dentin applying the CA APOSS adhesives was also determined. The effect of APOSS on the stability of CA adhesive against hydrolysis studied performing solubility, water uptake, and aging tests.

Results: The results revealed higher efficiency of BD in comparison to PPD. A 3% (mol/mol) of BD was obtained as the optimum photoinitiator concentration. The incorporation of APOSS increased the polymerization shrinkage rate of the CA adhesives. The flexural strength of CA adhesive was significantly improved incorporating less than 20 wt.% APOSS while an increasing trend was observed in the flexural modulus with the nanostructures loading. The microshear bond strength to dentin was also enhanced using 10 wt.% APOSS as reinforcing/ crosslinking nanofillers. A decrease in the solubility and water sorption was the result of incorporation of APOSS in CA adhesives. Degradation due to the hydrolysis in water was diminished in the specimens containing APOSS nanostructures, revealed after aging in water at 37 ◦C.    

Significance: CA adhesives are good soft tissue adhesives which their low mechanical properties and lack of hydrolytic stability has made them less interesting in the applications deal with hard tissues. The study shows that the incorporation of POSS nanostructures into CA could reduce the drawbacks.

Keywords: Cyanoacrylate adhesive , Polyhedral oligomeric , silsesquioxane (POSS) , Photopolymerization ,  Shrinkage , Physical and mechanical properties


Dental materials 29(2013)e61-e69

.

نفر دوم مقاله پژوهشی زیست مواد دندانی

In vitro degradation and bioactivity of poly(propylene Fumerate)/bioactive glass sintered micro-sphere scaffolds for bone tissue engineering


Sima Shahabi,Yashar Rezaei,*Fathollah Moztarzadeh,Farhood Najafi


Science and Engineering of Composite Materials November 2014



بایگانی مطالب:

مطالب کدام بخش سایت بیشتر مورد نیاز شماست؟
پرسش و پاسخ
جشنواره شهید هدایت
کلینیک تخصصی دندانپزشکی
مجله علمی
نمایشگاه کتاب
نمایشگاه مواد و تجهیزات دندانپزشکی
نیازمندیها
   
:. کل کاربران ثبت شده: 173
:. کاربران حاضر در وبگاه: 0
:. میهمانان در حال بازدید: 13
:. تمام بازدید‌ها: 12685963
:. بازدید 24 ساعت قبل: 2985

کلیه حقوق این وب سایت متعلق به جامعه اسلامی دندانپزشکان می باشد.

صفحه اصلی | درباره ما | ارتباط با ما | نقشه سایت

Created in : 0.04 seconds with 46 queries by YEKTAWEB